露石剂的作用机理研究
蔡正森,李立辉,陈喜旺,何哲
1.交通运输部公路科学研究院,100088,北京;2.河北工业大学土木与交通学院,300401,天津;3.道路及材料交通运输行业重点实验室(北京),100088,北京;4.北京建工新型建材有限责任公司,100021,北京
Study on Mechanism of action of aggregate exposing solvent
CAI Zheng-sen, LI Li-hui, CHEN Xi-wang, HE Zhe
1.Research Institute of Highway Ministry of Transport, 100088, Beijing, China; 2.Hebei University of Technology School of Civil Engineering and Transportation, 300401, Tianjin, China; 3.Roads and Transport Industry Laboratory Materials(Beijing), 100088, Beijing, China; 4.Beijing Construction Engineering Group New Building Materials Co., Ltd., 100021, Beijing, China
 全文: PDF (0 KB)   HTML (1 KB)  输出: BibTeX | EndNote (RIS)      背景资料
摘要 通过不同浓度梯度露石剂试验,并设置不同温度梯度的混凝土养护环境对比试验,设置基准组与添加露石剂的对照组进行混凝土水化热试验。结果表明:露石清扫时间和露石深度随露石剂浓度增加呈现增加趋势,但超过一定浓度值后清扫时间和清扫后的露石深度均不再增加;混凝土成型后,表面水膜消失速率随养护环境温度升高而逐渐加快,露石剂喷洒时间随之缩短。基准和添加露石剂的水泥混凝土随恒温养护时间增加,放热速率曲线均呈现先增加再降低的趋势,但添加露石剂的对照组放热速率最大值、最大放热速率、混凝土1 400 min的放热量均有所减小和推迟。
服务
把本文推荐给朋友
加入我的书架
加入引用管理器
E-mail Alert
RSS
作者相关文章
蔡正森
李立辉
陈喜旺
何哲
关键词道路工程   对比试验   水泥水化   露石剂     
Abstract: The experiment was carried out by using different concentration gradient of the aggregate exposing solvent test, and set up the concrete health environment with different temperature gradient, the concrete hydration heat test was carried out with the control group with the addition of aggregate exposing solvent. The results show that the cleaning time and the depth of EACCP is increasing with the increase of the concentration of aggregate exposing solvent, but they are not increased.,after the certain concrete, the disappearance rate of the surface water film increases with the increase of the temperature of the health environment, and the spraying time of the terring agent is shortened. The hydration heat release rate of the cement concrete of the addaggregate exposing solvent groups and unadded groups increased with the increase of the constant temperature, and the exothermic rate curves show a tendency to increase first and then decrease. However, the maximum exothermic rate, the maximum exothermic rate and the heat release rate of concrete 1 400 min were reduced and delayed of the addaggregate exposing solvent groups.
Key wordsroad engineering   comparative test   cement hydration   aggregate exposing solvent   
引用本文:   
蔡正森,李立辉,陈喜旺等. 露石剂的作用机理研究[J]. 建筑技术, 2017, 48(10): 1052-.
CAI Zheng-sen,LI Li-hui,CHEN Xi-wang et al. Study on Mechanism of action of aggregate exposing solvent[J]. Architecture Technology, 2017, 48(10): 1052-.
链接本文:  
http://www.jzjs.com/CN/     或     http://www.jzjs.com/CN/Y2017/V48/I10/1052
 
没有找到本文相关图表信息
没有本文参考文献
[1] 李学勋,陈奕柏,李东海. 粘贴碳纤维布或增大截面加固梁现场荷载试验分析[J]. 建筑技术, 2017, 48(4): 430-433.
?
版权所有 © 2011 建筑技术杂志社
地址:北京市广莲路1号建工大厦A座9层,邮编100055 电话:(010)68512449 (010)63928687,63928688 e-mail:jzjs@sina.com
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn